| Foring Ratio: | ≥3.5 | Melting Process: | EF+LF+VD |
|---|---|---|---|
| Heat Treatment: | N+T Q+T | Application: | Machinery Parts |
| Size: | As Drawing | Color: | Original |
9Cr2Mo High Speed Forged Steel Rolls EN Standard Hot Roller Forging
Products: hot forging roller,overall roller,hot roll shaft,high speed roller,wearproof roller ,high Cr roller.
Products reference:
| Material | 50Mn,4140,60CrMo,9Cr2Mo,90Cr3 |
| Forging equipment | 8000T open die hydropress |
| 申し込み |
Hot roller is mainly used for rough mill of hot rolling sheet |
| Melting process | EF+LF+VD |
| Production process |
Forging+heat treatment+rough machining+QT |
| Foring ratio |
≥3.5 |
| Applicable standard | ASTM,ASME,IN,JIS,ISO,BS,API,EN |
| Executive standard | JB/GB/EN/DIN/JIS/ASME/ASTM/ISO |
|
Certification authority |
ISO9001:2008,BV,SGS, IST, UL,CTI |
| Delivery term |
Rough machining(N+T);finish mahcining(Q+T) |
| Test equipment |
Spectrograph,ut device,tensile and compact test machine,metalloscope,outside micrometer,bore dial indicator,hardness test machine |
| Service | Our service included the forging, process, heat treatment, finish machining, package, local logistics, customers clearance and maritime transport. We took the customer’s requirements as the principal thing, and pay attention on the products quality. |
Custom properties
| Material elements | C | Si | Mn | P | S | Cr | Ni | Mo |
Others |
| 50Mn2 | 0.48-0.56 | 0.17-0.37 | 1.6-2.3 | ≤0.035 | ≤0.035 | ≤0.25 | ≤0.30 | ≤0.25 | |
| 4140 | 0.38-0.43 | 0.15-0.35 | 0.60-0.90 | ≤0.035 | ≤0.040 | 0.80-1.10 | — | 0.15-0.25 | – |
| 60CrMo | 0.55-0.65 | 0.17-0.30 | 0.450-0.80 | ≤0.020 | ≤0.015 | 0.50-0.80 | ≤0.25 | 0.20-0.40 | |
| 9Cr2Mo | 0.85-0.95 | 0.25-0.45 | 0.20-0.40 | ≤0.025 | ≤0.025 | 1.70-2.10 | ≤0.25 | 0.20-0.40 |
|
Mechanical property |
Dia.(mm) |
TS/Rm(Mpa) |
YS/Rp0.2(Mpa) |
EL/A5(%) |
RA/Z(%) |
Type Of notch |
Impact energy |
HBW |
| 50Mn2 | Ø25 | ≥930 | ≥785 | ≥9 | ≥40 | V | ≥39 | ≤229HBS |
| 4140 | Ø25 | 740~1000 | 450~850 | ≥12 | ≥25 | V | ≥40 | ≤250HBS |
Process procedure: Forging process flow quality control: Raw material steel ingot into warehouse(test the chemical content) → Cutting→ Heating(Furnace temperture test) → Heat treatment after forging(Furnace temperture test) Discharge the furnace(blank inspection)→ Machining→ Inspection(UT,MT,Visal diamention, hardness)→ QT→ Inspection(UT, mechanical properties, hardness, grain size)→ Finish machining→ Inspection (dimension)→ Packing and Marking(steel stamp, mark)→ Storage Shipment
Commerce clause
| MOQ | 1PC |
| MAX diameter | 1600MM |
| Delivery time | 30-60 Days |
| Package | wood pallet,steel frame |
| Delivery term | FOB;CIF;CFR；DDU； |
| Payment terms | T/T,LC |
| Type of shipping |
By ocean,air |