1.ASTM A681 H11 Tool Steel Supply Range
H-11 Steels Round Bar: diameter 8mm–1000mm
H11 Steel Flat: thickness 16-500mm x width 200-800mm
H11 Steels Plate: thickness 16-500mm x width 200-810mm
Other dimension according to your requirements
表面仕上げ
Black, Rough Machined, Peeled, Turned or as per given requirements.
2.AISI H11 Tool Steel Standard and Relevant Steel Specifications
| 国 | アメリカ | ドイツ語 | 日本 | British |
| 標準 | ASTM A681 | DIN EN ISO 4957 | JIS G4404 | BS 4659 |
| 学年 | H11/T20811 | 1.2343/X37CrMoV5-1 | SKD6 | BH11 |
3.H11 Tool Steel and Equivalents’ Chemical Composition
| ASTM A681 | C | Mn | P | S | Si | Cr | V | W | Mo | ||||||
| H11/T20811 | 0.35 | 0.45 | 0.20 | 0.60 | 0.03 | 0.03 | 0.80 | 1.25 | 4.75 | 5.50 | 0.30 | 0.60 | … | 1.10 | 1.60 |
| DIN ISO 4957 | C | Mn | P | S | Si | Cr | V | W | Mo | ||||||
| 1.2343/X37CrMoV5-1 | 0.33 | 0.41 | 0.25 | 0.5 | … | … | 0.80 | 1.20 | 4.8 | 5.5 | 0.3 | 0.5 | … | 1.10 | 1.50 |
| JIS G4404 | C | Mn | P | S | Si | Cr | V | W | Mo | ||||||
| SKD6 | 0.32 | 0.42 | … | 0.50 | 0.03 | 0.03 | 0.80 | 1.20 | 4.50 | 5.50 | 0.30 | 0.50 | … | 1.00 | 1.50 |
| BS 4659 | C | Mn | P | S | Si | Cr | V | W | Mo | ||||||
| BH11 | 0.32 | 0.40 | … | 0.40 | 0.35 | 0.35 | 0.85 | 1.15 | 4.75 | 5.25 | 0.30 | 0.50 | … | 1.25 | 1.75 |
4. H11 Hot Work Tool Steel Properties
物理的性質
| プロパティ | メートル法 | インペリアル |
| 密度 | 7.81 g/cm3 | 0.282 lb/in3 |
| 融点 | 1427°C | 2600°F |
機械的特性
| プロパティ | メートル法 | インペリアル |
| Hardness, Rockwell C (air cooled from 982°C, 45 mins) | 52.5 | 52.5 |
| Hardness, Rockwell C (air cooled from 1010°C, 45 mins) | 56 | 56 |
| Hardness, Rockwell C (air cooled from 1038°C, 45 mins) | 57 | 57 |
| Modulus of elasticity | 207 GPa | 30000 ksi |
| Modulus of elasticity (@538°C/1000°F) | 159 GPa | 23000 ksi |
| Modulus of elasticity (@204°C/400°F) | 190 GPa | 27500 ksi |
| Charpy impact (V-notch; air cooled from 1010°C;535°C temper temperature) | 13.6 J | 10.0 ft-lb |
| Charpy impact (V-notch; air cooled from 1010°C;650°C temper temperature) | 27.1 J | 20.0 ft-lb |
| Charpy impact (V-notch; air cooled from 1010°C;370°C temper temperature) | 33.9 J | 25.0 ft-lb |
| Machinability (1% carbon steel) | 75.0 – 80.0% | 75.0 – 80.0% |
| ポアソン比 | 0.27-0.30 | 0.27-0.30 |
熱的特性
| プロパティ | メートル法 | インペリアル |
| Thermal expansion (@20-100ºC/68-212ºF) | 11.9 x 10-6/ºC | 6.63 µin/in°F |
| Thermal conductivity (@100ºC/212ºF) | 42.2 W/mK | 292.9 in/hr.ft².°F |
5. Forging of H11 Tool Steels
AISI H11 alloy steels are forged at 1121°C (2050°F). For this type of steels, forging below 899°C (1650°F) is not preferable.
6.AISI H11 Tool Steel Heat Treatment
Annealing of H-11 steel
Anneal at 871°C and slow cool at 4.4°C per hour or less in the furnace.
Tempering of Steel H11
Temper at 537°C to 648°C for Rockwell C hardness of 54 to 38. Double tempering for one hour each time at the selected tempering temperature is recommended.
7.Applications of AISI H11 Tool Steel
H11 alloy steel is often used for highly stressed structural parts such as aircraft landing gear.
Some typical applications: Hot punches, die casting dies, forging dies, hot shear blades, hot gripper dies, and extrusion tooling.
The tools produced from H11 chromium hot-work steels can be cooled using water without damage as these steels have low carbon and alloy contents.
We are reliable supplier of AISI H11 tool steel and we offer and delivery satisfactory quality of H-11 tool steel. Contact us for best offer of AISI H11 steel materials.