D6 steel is a high-carbon, high-chromium tool steel commonly used in manufacturing and tool making applications. It contains 1.4-2.2% carbon and 11-13% chromium, which gives it excellent wear resistance, toughness, and dimensional stability. D6 steel is often used in forging dies, shear blades, cold and hot work tooling, and other applications where high wear resistance and excellent dimensional stability are required.
| SIMILAR STEEL GRADES | ||||||
| National Standard | Manufacturer Standard | |||||
| GB | AISI | DIN | JIS | Erasteel | Bohler | Hitachi |
| *Cr12W | D6 | 1.2436 | SKD2 | – | – | – |
| Chemical composition % | ||||||||||
| C | Si | Mn | P ≤ | S ≤ | Cr | W | Mo | V | Co | etc. |
| 2.10 | 0.35 | 0.35 | 0.030 | 0.03 | 12.00 | 0.7 | – | – | – | |
| Characteristics | |||
| Annealed Hardness HB | Heat Treatment Temperature ℃ | Tampering Hardness HRC | |
| Hardening | Tempering | ||
| 255 | 950-980 | 200 | 61-63 |
A liga de aço SAE 4140 é uma liga versátil com boa resistência à corrosão atmosférica e resistência mecânica razoável. Apresenta uma boa combinação global de resistência mecânica, tenacidade, resistência ao desgaste e resistência à fadiga.
O aço D2 é um aço para ferramentas de alto teor de carbono e crómio, que endurece ao ar. Possui elevadas propriedades de resistência ao desgaste e à abrasão. É submetível a tratamento térmico, atingindo uma dureza na gama de 55 a 62 HRC, e é usinável em…